Bright short-wavelength infrared organic light-emitting devices

Organic LEDs that emit light in the short-wavelength infrared (SWIR) region, which spans the 1–2 μm region, are attractive for applications in biosensors, biomedical imaging and spectroscopy, and surveillance. However, fabrication of such devices with high radiance has not yet been achieved owing to an intrinsic limitation imposed by the energy-gap law, which leads to extremely low emission efficiencies. Here, we report that acceptor–donor–acceptor-type molecules with high coplanarity, rigid π-conjugated backbones, an extremely small reorganization energy and an electron–phonon coupling factor are capable of simultaneously providing a strongly suppressed non-radiative recombination rate and a high operation stability at high current density. We achieve electrically driven SWIR organic LEDs with an irradiance of up to 3.9 mW cm−2 (corresponding to 7% of direct sunlight infrared irradiance). These findings should open a wide avenue to a new class of organic SWIR light sources for a broad range of applications. Organic LEDs based on acceptor–donor–acceptor molecules Y11, IDSe-4Cl and COTIC-4F are shown to be highly effective emitters of short-wave infrared light.

O rganic semiconductors with advantageous electronic and optoelectronic properties have enabled the demonstration of high-performance organic light-emitting devices (OLEDs) with emission covering the visible, near-ultraviolet and near-infrared (NIR) parts of the electromagnetic spectrum [1][2][3][4][5] . There has been a long-standing demand for the development of electrically driven SWIR (that is, 1,000-2,000 nm) 6,7 light sources in view of their broad range of applications, including optical communications [3][4][5] , night-vision surveillance 3,4,6 and remote sensing 8 . Recent emerging applications in biological imaging [9][10][11] , medical analysis 12 and infrared spectroscopy 9 for health, food and environmental monitoring have required the development of bright, biocompatible SWIR emitters since longer imaging wavelengths promise lower light scattering, a deeper tissue penetration depth and superior spatiotemporal resolution 9-11 compared with the visible and NIR (700-1,000 nm) counterparts. More recently, SWIR light sources have been integrated in smartphones for providing security authentication and photonic sensing functionalities 4,13 , thereby enabling fast and convenient face and iris recognition. Currently, high-performance SWIR emitters are generally made from group III-V compound semiconductors 7,14 using molecular beam epitaxy or metal organic chemical vapour deposition. Compared with other solution-processable alternatives 7 , two major hindrances for these SWIR light sources are their point source characteristics 15 , with typical diameters of a few hundreds of micrometres, and their low degree of mechanical flexibility 16 , owing to the high Young's modulus (for example, ~130 GPa for silicon), which limit their potential applications in wearable and implanted electronic devices.
Among the emerging candidates for large-area planar SWIR light sources, OLEDs have been identified as particularly unique since they have the combined advantages of high-throughput fabrication at extremely low costs, being lightweight, having mechanical flexibility, tunable chemical, physical and emission-wavelength properties, and being compatible for use in large-area devices [1][2][3] . Furthermore, purely organic fluorescence emitters are free of heavy metals, which increases their biocompatibility and environmental sustainability, thus making them ideal for health, food and environmental applications where biocompatibility, toxicity and environmental issues must be considered 4 . To translate these advantages to widespread SWIR applications, high-radiance/brightness OLEDs are necessary for obtaining a satisfactory performance and for device miniaturization. However, unlike their success in the visible 1 and NIR regions [3][4][5]13,17,18 , bright OLEDs in the SWIR range have not been demonstrated so far. The main reason for this could be ascribed to the limitation imposed by the energy-gap law [3][4][5] , which predicts an exponentially increased non-radiative decay rate with decreasing energy gap in organic solids as a result of increased electron-phonon coupling between the excited and ground states. This limitation indicates that, if the energy-gap law is strictly valid, long-wavelength emission from organic solids is extremely weak and there is a major bottleneck for extending the emission to longer wavelengths.
Despite such a major fundamental hurdle, extensive research efforts have been devoted to narrowing the energy gap and realizing electroluminescence (EL) beyond the visible region, that is, 700-1,000 nm NIR emission in organic solids [3][4][5] , by adopting rational strategies that are used for visible emitters. These strategies generally involve several key considerations [3][4][5] , such as extending the conjugation length, reducing bond length alternation (corresponding to greater π-electron delocalization), the introduction of appropriate donor-acceptor charge-transfer units and the use of triplet 19 or doublet excitons 20 . As a result, organic emitters that are available nowadays for NIR OLEDs include mainly organometallic phosphorescent complexes 21,22 , organic ionic dyes 23 , conjugated polymers 24 , organic compounds containing donor-acceptor charge-transfer chromophores 3,5,18,[25][26][27] , thermally activated delayed fluorescent materials 28 and doublet emitters 20 . In 2020, Wei et al. reported state-of-the-art phosphorescent NIR OLEDs by exploiting a series of 5-(2-pyridyl)pyrimidinate Pt(II) complexes, achieving an EL emission maximum at 930 nm, with an external quantum efficiency (EQE) of 2.14% and a remarkable maximum radiant exitance of 13.06 mW cm −2 (ref. 22 ). Yu et al. demonstrated high-performance fluorescent NIR OLEDs based on anthracene-cored emitters, which exhibit EL peaks at 838 nm and 916 nm with EQE values of 0.58% and 0.07%, while the maximum radiant exitance is 2.8 mW cm −2 and 0.29 mW cm −2 , respectively 29 . More recently, progress in fluorescent NIR OLEDs has been made by Minotto et al., who achieved an EQE of 1.1% with an EL emission maximum at 850 nm and a maximum radiant exitance of 1.9 mW cm −2 (ref. 13 ). However, previous studies have shown that OLEDs emitting at longer wavelengths (for example, beyond 1,000 nm and extending into the SWIR region) always suffer from severe non-radiative recombination loss, leading to low EQE values of the order of 0.01% (refs. 24,30 ). In 2009, Qian et al. reported a series of pure organic emitters based on a benzobisthiadiazole derivative that emitted at wavelengths beyond 1,000 nm (ref. 3 ). Non-doped devices based on a chromophore featuring triphenylamine derivatives as the acceptor group exhibited a state-of-the-art EQE of 0.28% and an EL peak at 1,080 nm, with a maximum radiant exitance around 0.06 mW cm −2 . Although the radiant exitance and EQE of an OLED based on a different chromophore were too low for practical applications, its EL peak at 1,220 nm was one of the longest emission wavelengths for pure organic emitters reported so far, demonstrating the promising potential of organic chromophores as SWIR emitters for further development. Ever since the recent emergence of a new class of aromatic fused-ring electron acceptors with an acceptor-donor-acceptor (A-D-A) structure, the development of organic solar cells has entered into a new era, featuring the coincidence of efficient charge separation and low voltage losses 31 . Owing to the strong intramolecular charge-transfer effect and the rigid planarity configuration of the fused rings, the π-electron delocalization in these A-D-A-type organic semiconductors is enhanced, producing a reduction in the bandgap and a greater oscillator strength that increases the NIR absorption coefficient. Moreover, A-D-A-type organic semiconductors show several additional great merits that are essential for minimizing energy losses in organic solar cells. These include a sharp optical absorption edge, a suppressed non-radiative recombination rate, low energetic disorder and a high luminescence (radiative recombination) yield, which play an important role in obtaining a high photovoltage 32 . According to the reciprocity relationship that exists between light absorption and emission 33 , such organic semiconductors that are ideal for solar cells are likewise ideal for LEDs.

results and discussion
Computational results. Before attempting to exploit A-D-A-type organic semiconductors for SWIR emitter applications, density functional theory (DFT) and time-dependent DFT (TD-DFT) approaches at the ωB97XD/6-31G(d,p) level with the optimally tuned ω parameter were used to study the structural regularity and excited-state properties for three typical narrow-bandgap molecules with low photon energy loss in organic solar cells, that is, Y11 (ref. 32 ), IDSe-4Cl (Supplementary Methods) and COTIC-4F (ref. 34 ) (see Fig. 1a-c for chemical structures and the Methods section for computational details). Our DFT calculation results displayed a small dihedral angle of 14° for Y11, whereas nearly planar structures with negligible torsion in their relaxed geometries were observed for IDSe-4Cl and COTIC-4F ( Supplementary Fig. 1). The success of this design strategy was confirmed via the extended emissive exciton wavefunctions, as shown by the calculated natural transition orbitals (NTOs) that describe the first singlet (S 1 ) excited states (see Fig. 1d). The NTO hole and electron wavefunctions of the S 1 excitons are spread over the whole π-conjugated backbones, implying strong electronic couplings between the donor and acceptor moieties. In conjunction with the alternating electron-withdrawing and electron-releasing moieties that incur an intramolecular charge-transfer effect 4,5 , the enhanced wavefunction delocalization and the extended planarity of the A-D-A molecules ensure minimized optical bandgap energies 35 (E g ) of 1.37, 1.27 and 1.17 eV for Y11, IDSe-4Cl and COTIC-4F, respectively ( Supplementary Fig. 2), which is envisaged to lead to SWIR emissions beyond 1,000 nm. More importantly, the significant spatial overlaps (O h/e ) between the NTO-hole and NTO-electron give rise to very large oscillator strength (f) values of 2.3, 3.2 and 3.0 for Y11, IDSe-4Cl and COTIC-4F, respectively 36 , corresponding to their high radiative recombination rates, as discussed below.

Photophysical properties and numerical simulations.
To further illustrate their potential as a new type of SWIR emitter, the absorption and photoluminescence (PL) spectra of the three molecules were measured. As shown in Fig. 2a-c, the thin-film spectra of the three molecules exhibit sharp absorption bands with a dominant peak slightly above the optical gap and a low-energy shoulder adjacent to it. Owing to its overwhelmingly high oscillator strength, transition from the ground state (S 0 ) to the first excited state (S 1 ) induces an intense absorption peak, which, consequently, surpasses the intensities of other transitions. Following Kasha's rule, fast thermalization to the first excited state occurs before transition that leads to radiative recombination could take place, such that the higher energy electronic transitions should play a minimal part in the PL, and the PL spectra are dominated by the S 1 → S 0 transition only. The low-energy shoulders found in the PL spectra are thus confirmed to be an outcome of high-frequency vibrational modes of the molecules 37,38 .
Meanwhile, we propose a model based on established theories 39-41 to describe these vibrational pathways through which unfavourable non-radiative recombination takes place. According to the model, the optical emission intensity I emission at a specific photon energy hν (h, Planck's constant; ν, photon frequency) is proportional to the oscillator strength f that embodies the electronic transition dipole moment as well as the Franck-Condon-weighted density of states (FCWD) that describes the wavefunction overlap between the vibrational levels of excited and ground states, while adopting the Born-Oppenheimer approximation (Supplementary Note 1): with in which k B is the Boltzmann constant and T is the temperature.
Here, FCWD(hν) is further governed by three vibrational parameters: the low-frequency reorganization energy λ s that describes the conformational changes of the molecule and its surroundings upon excitation; the energy of the high-frequency vibrational mode hνv in which ν v is the average of the frequencies of atomic vibrations within the molecule; and the electron-phonon coupling factor S, which is related to the high-frequency reorganization energy λ v that results from atomic displacements upon charging to the aforementioned mean phonon energy hνv by S = λv/(hνv). The lineshape of the reduced emission spectra where the emission spectra are divided by (hν) 3 are therefore intricately modulated by these vibrational parameters through equation (2). Careful fitting of the measured PL spectra via equations (1) and (2) enabled the extraction of vibrational parameters for our molecules, as shown in Fig. 2d-f, with details provided in Supplementary Note 2. Very low λ s values ranging from 0.045 to 0.06 eV are obtained for these molecules, which correspond to their narrow linewidths. The observations are also consistent with the noticeably reduced Stokes shifts, as indicated in Fig. 2a-c. Overall, these findings suggest that photo-excitation and the subsequent decay barely trigger the deformation of their molecular geometry, which is a result of the enhanced planarity and rigidity of these A-D-A molecules. Owing to their narrow linewidths, the mean phonon energy hνv, which ranges from 0.12 to 0.14 eV for the molecules, can be readily determined via the small energy shift from the pronounced 0-0 peaks to the 0-1 vibrational shoulders ( Supplementary Fig. 3). As such, the experimental values are considerably lower than the characteristic value of 0.16 eV for the predominant carbon-carbon bonds and ring-stretching modes in organic molecules 37,40,42 . Finally, values for the electron-phonon coupling factor S in the range of 0.7-0.9 are extracted for the molecules. Through fitting of the emission spectrum lineshapes, the obtained values of 0.17, 0.14 and 0.15 eV for Y11, IDSe-4Cl and COTIC-4F, respectively, for the estimated total reorganization energy (λ S 1 = λs + λv), which includes the two parts due to the low-and high-frequency vibrations, are highly consistent with our TD-DFT calculation results, that is, 0.13, 0.13 and 0.15 eV, respectively, indicating the reliability of our fitting via equations (1) and (2).
Substituting all the previously obtained parameters into Fermi's golden rule, the rate constant of non-radiative recombination k nr can be derived: with the electronic coupling V c approximated by the generalized Mulliken-Hush method 41,43 (Supplementary Note 1). The photoluminescence quantum yield (PLQY) can eventually be determined via PLQY = kr kr+knr , where k r is the rate constant of radiative recombination. The calculated PLQY values for a set of representative parameters are plotted against the bandgap in Fig. 2g. The PLQY data show a dramatic decrease as the bandgap is lowered, following the energy-gap law, leading to a lower PLQY for narrow-bandgap molecules. The results of experimentally determined PLQY values are included in this figure for direct comparison. Nevertheless, further numerical simulations show that the reduced λ s , hνv and S values of the molecules reported herein significantly suppress the rate constant for non-radiative recombination  , total reorganization energy ( λ S 1 = λs + λv), which includes the two modes due to low-frequency (λ s ) and high-frequency (λ v ) vibrations, the oscillator strength (f) and overlap between NTO electron and hole orbitals (O h/e ) for the first singlet (S 1 ) excited states of Y11, IDSe-4Cl and COTIC-4F, calculated at the ωB97XD/6-31G(d,p) level using the optimally tuned ω parameter. For computational details, see the Methods section. Fig. 4), whereas an enhanced oscillator strength f is beneficial for an increased rate constant for radiative recombination, eventually giving rise to higher PLQY values for the molecules (calculated values of 0.1-10% for bandgaps ranging from 1.1 to 1.3 eV). It is worth noting that the PLQY values of Y11, IDSe-4Cl and COTIC-4F in dilute solutions are measured to be 17.3%, 3.26% and 3.28%, respectively, which show a noticeable increase along with their broadened energy gap, which is also predicted by the proposed model ( Supplementary Fig. 5). These results demonstrate that aggregation of the studied molecules in films plays a role in reducing their emissive efficiencies. Interestingly, the extent of decrease in PLQY for the three molecules is very different, which is related to their molecular packing in the films. As demonstrated in previous investigations, the aggregation effect on the emissive efficiency is impacted by several potential factors 22 (for example, a reduction of the effective reorganization energy due to exciton delocalization, or the suppression of non-adiabatic electron-vibration coupling).

(Supplementary
Under these circumstances, A-D-A molecules with conjugation extension 44 and/or enhanced planarity and rigidity in their π-conjugated backbones 45 , as well as increased non-bonding interactions between molecular fragments that enable reduced reorganization energies, are indeed ideal candidates that are capable of enhancing the long-wavelength emission and the emission efficiency simultaneously. To make further improvements in the PLQY, other approaches, such as heavy-atom substitution (for example, selenium substitution, as introduced in our IDSe-series molecules) or halogenation for retarding high-frequency vibration modes, could be an effective molecular-design strategy to lower the mean phonon energy hνv in A-D-A molecules, as discussed below.
Although the k nr values for the series of A-D-A-type organic semiconductors extracted from experimentally determined PLQY (Supplementary Table 1) and time-resolved PL decay transients ( Supplementary Fig. 6) increase with decreasing bandgap, this is much less pronounced compared with the prediction of the   (1), the corresponding curves fitted by multiple Gaussian peaks, and the emission spectra modelled using equation (2), with the extracted parameters as input also being shown. g, The modelled PLQY data using specific photophysical parameters extracted from Y11, IDSe-4Cl and COTIC-4F plotted as a function of the optical gap, where their experimentally measured PLQY values are shown as scattered dots for comparison.
energy-gap law (Fig. 3a). In addition, the extracted k r data show a striking increase with increasing oscillator strength (Fig. 3b), which is consistent with the model calculations ( Supplementary  Fig. 4g). The features shown in Fig. 3a  IDSe-4F c Fig. 3 | rate constants of radiative and non-radiative recombination and PLQY as well as their correlations with the microscopic parameters. a-c, Rate constants of non-radiative recombination k nr (a) and radiative recombination k r (b) for solid films and PLQY (c) as a function of the optical bandgap with respect to variation in the oscillator strength f (electronic coupling V c ), low-frequency reorganization energy λ s and mean phonon energy hνv while the electron-phonon coupling factor S is fixed at 0.8. The electronic coupling V c is related to f via the generalized Mulliken-Hush method 41,43 . The symbols denote data points for non-radiative and radiative recombination rate constants extracted from analysis of the time-resolved PL measurements and PLQY values for a set of representative A-D-A-type molecules and a fullerene derivative as knr = 1 τ − kr and kr = PLQY τ . The chemical structure of the molecules are included in the Supplementary Information. The symbols and error bars represent the mean value ± one standard deviation across six measurements for each emitter (Supplementary Table 1). The PLQY measurements were carried out under ambient conditions. current density-radiance-voltage (J-R-V), EL spectra and EQE dependence on the current density (EQE-J), are shown in Fig. 4 and Supplementary Fig. 9, while the key parameters are summarized in Table 1. The influence of doping on the EL properties was also investigated in OLEDs based on an emitting layer containing a typical host material blended with the SWIR emitters at various doping concentrations, with the device characteristics of the optimized COTIC-4F and IDSe-4Cl devices shown in Supplementary  Fig. 10 and the corresponding device parameters summarized in Supplementary Table 2. The EL spectra of the COTIC-4F devices undergo a remarkable blueshift upon doping, with peaks at 1,200 nm for the COTIC-4F neat film, 1,060 nm for the 70 wt% film, 1,030 nm for the 50 wt% film and 1,010 nm for the 30 wt% film, where a similar trend is also observed in the IDSe-4Cl devices. The blueshift in the EL spectra can be attributed to the polar surrounding effect that leads to a gradual decrease in the surrounding polarity with a decreasing doping concentration of emitters with good planarity 29 . It is noteworthy that the maximal EQE for the doped COTIC-4F device is 0.059%, which is approximately twice that of the best non-doped COTIC-4F device (0.031%), while the doped IDSe-4Cl devices show a decreased EQE of 0.079% compared with the that for non-doped device (0.13%), which is probably as a result of the different variation of charge-transport properties between the emitting layers, as evidenced by the change in the turn-on voltage V on (Supplementary Table 2). The EL spectra of the devices demonstrate tuning with the peak ranging from 810 to 1,230 nm (Fig. 4a).
It is worth noting that OLEDs based on i-IDSe-4Cl (with an emission peak at 843 nm) and Y11 (a peak at 945 nm) show a maximum EQE of 0.54% and 0.33%, respectively (Table 1), which are among the highest efficiencies reported in fluorescent NIR OLEDs 29 . Moreover, these devices exhibit a high maximum radiant exitance of 8-14 mW cm −2 , which is twice that of the best fluorescent emitter 29 and comparable to state-of-the-art phosphorescent NIR OLEDs with similar EL spectra ( Supplementary Fig. 11) 22 . More importantly, the broad tunability of the A-D-A-type organic semiconductors has enabled bright SWIR EL that spans 1,000 to 1,300 nm and beyond, which is extremely rare in organic material systems. Among them, devices based on IDSe-4F and IDSe-4Cl show the best performance (Table 1), which have EQE values of 0.12% and 0.13% with EL peaks at 1,080 nm and 1,110 nm, respectively. These two molecules are analogues of the reported ultranarrow-bandgap A-D-A-type conjugated molecules 46 in which indacenodiselenophene (IDSe) is used as the electron-donating core to achieve redshifted absorption and large extinction coefficients 47 . Besides, a long branched alkoxy group was introduced to the inserted thiophene unit to provide good solubility for improved film quality in OLEDs. It is important to note that the EQE values of IDSe-4F and IDSe-4Cl are sevenfold higher than that of their molecular analogue TTT-C20-4F (~0.017%, Table  1), highlighting the importance of retarding the high-frequency vibration modes through heavy-atom substitution.
The superior device performance is also evident in the current density-radiance-voltage (J-R-V) characteristics, as shown and EQE versus current density curves (c) of the SWIR OLEDs. EL spectra for devices with emission peaks between 700 nm and 1,000 nm were recorded using a spectrometer-calibrated silicon detector. EL spectra for devices with emission peaks past 1,000 nm were recorded using a spectrometer equipped with calibrated InGaAs line detector. d, Photograph of a 15 × 15 mm IDSe-4Cl OLED at a current density of 22 mA cm −2 , taken using an InGaAs camera.
in Fig. 4b, where the current density and radiance values increase exponentially by orders of magnitude after turn-on, reaching very high radiances of 12.2 W sr −1 m −2 at 3.6 V in the IDSe-4F device and 12.4 W sr −1 m −2 at 4.2 V in the IDSe-4Cl device. These encouraging radiance values correspond to a high radiant exitance (irradiance) of 3.8-3.9 mW cm −2 (corresponding to a 0.07 Sun direct sunlight infrared irradiance that is 51 mW cm −2 ), which is a dramatic enhancement of 60-fold compared with the best reported organic emitter with similar EL spectra 3 and the brightest SWIR OLEDs so far (Supplementary Table 3 and Supplementary Fig. 11). Interestingly, the turn-on voltage (V on , the voltage at which a radiance of 1 mW sr −1 m −2 is detected) of the IDSe-4F and IDSe-4Cl devices is as low as 1.02 ± 0.076 V and 0.95 ± 0.055 V, respectively, which is essentially below the nominal emitted photon voltage (~1.1 V, defined as V ph = hν/e, where hν is the emitted photon energy, e is the elemental charge). The EL emission at subgap voltages is also observed in other A-D-A-type NIR/SWIR emitters (Table 1 and Supplementary Fig. 9), among which the COTIC-4F device achieved a V on of 0.78 ± 0.041 V, which is obviously lower than the V ph of 1.14 V and is the lowest reported one in the whole OLED field so far.
Owing to thermodynamic constraints, EL emission at voltages below the emitted photon energy is hardly ever accessible but can occur without violating the energy-conservation law through the recombination of diffusion-driven and thermally generated charge carriers 48 . Under any voltage above 0 V, a diffusion current due to the gradient of the carrier concentrations starts to flow, following an exponential dependence on the applied voltage. According to the mechanism, it was demonstrated that once charge recombination is dominated by the diffusion of charge carriers, rather than by the drift current, while the accumulation of majority carriers takes place at the same time, emissive Langevin recombination can become apparent even when at subgap voltages. In our devices, barrier-free hole injection into the emissive layer leads to hole accumulation at the active layer/cathode interface, while a relatively small built-in potential gives rise to the establishment of a positive drift current at low forward bias ( Supplementary Fig. 12). It is equally important to note that the recombination rate k Rec in the diffusion-dominated regime is inversely proportional to an exponential dependence on the bandgap 48 , where γ is the bimolecular recombination coefficient and N C is the the effective density of states in the conduction band. Therefore, the recombination rate in our low-bandgap devices is sufficiently high to fulfil the condition for diffusion-dominated recombination to occur, leading to the EL emission at subgap voltages. The conclusion of diffusion-dominated current in our devices is further supported by the calculated diffusion current using the Shockley equation and numerical drift-diffusion simulations ( Supplementary Fig. 13a), both of which use the same set of extracted charge mobility data as input parameters ( Supplementary Fig. 13b-d). With the validation of the diffusion-dominated current description, the bandgap of the emitters contributes to the exponential part of the current while their charge-transport properties contribute to the linear part of the current. It is noteworthy that all devices can operate up to a high current density of 2,000-3,000 mA cm −2 (Fig. 4c and Supplementary Fig. 9), which was challenging to realize in previous NIR/SWIR OLEDs. The detailed physical picture that leads to such a high current density tolerance is far from clear; however, it is likely to stem from the short exciton lifetime of the emitters 29 (55-600 ps, Supplementary  Table 1), which are beneficial for preventing the accumulation of formed excitons and thus alleviating their concomitant loss, such as via Auger recombination and exciton-exciton annihilation at high carrier injection. Moreover, our non-doped devices promise sufficient recombination sites where injected carriers can recombine, thus avoiding saturation at low current density. In addition, the driving voltage values for the high current density (for example, 1,000 mA cm −2 ) in our devices are extremely low (2.2 V for SiOTIC-4F/COTIC-4F, 3.2 V for Y11/Y6 and 3.0 V for IDSe-4F/ IDSe-4Cl devices, see Supplementary Fig. 9j,f and Fig. 4b, respectively), which generate smaller Joule heating when compared with other reported OLEDs and thus sufficiently decrease additional exciton dissociation. Moreover, this high current density corresponds to a carrier density of around 10 18 cm −3 , which is a threshold for lasing under electrical excitation 49 . Interestingly, with increasing current density, the EQE values for all devices except those based on larger bandgap materials (for example, Y11 and i-IDSe-4Cl) demonstrate a remarkable increase, which ultimately gives rise to a high SWIR radiance. This dependence of EQE on current density is particularly striking as it implies that radiative recombination can compete with non-radiative recombination at high current densities in the OLEDs. One possible interpretation for this unusual dependency is that it corresponds to a trap-filling process with increasing voltage that not only shifts the recombination zone away from the electrode but also eliminates the non-radiative trap-assisted recombination, leading to an EQE enhancement of more than a factor of two in most devices. The injection-dependent EL spectra shown in Supplementary Fig. 14 are consistent with a recent study by Blom and colleagues, who reported that a voltage-dependent EL is a fingerprint of trap-assisted recombination 50 , and thus confirms the interpretation that radiative recombination dominates over competing trap-assisted recombination with increasing current density. In this manner, the A-D-A-type organic semiconductors possess the potential to fundamentally overcome the SWIR lasing boundary set by the high-excitation-threshold requirement and efficiency roll-off at high current density.
To demonstrate the potential of our technology, we fabricated large-area SWIR OLEDs based on IDSe-4Cl/IDSe-4F. Figure  4d shows a photograph of a typical IDSe-4Cl device with a peak emission wavelength at 1,110 nm and a SWIR radiation power of ∼0.6 mW at a current density of 22 mA cm −2 , which shows a remarkable emission uniformity over the substrate area with a size of 15 × 15 mm. The large-area device possesses a high maximum SWIR output power of ~8.8 mW, which is comparable to 10 mW as seen for InGaAs-based LEDs. These results demonstrate the promise of our devices as a cost-efficient flat-panel light source for applications in portable spectrometers, information-secured  displays and night-vision target identification. To provide visualization for these applications, we set up an optical wireless communication system (see Methods for the setup and Supplementary Fig.  15 for the simplified block diagram) in which our SWIR OLEDs are integrated as the transmitter for a free-space data link. Transmitting audio signals or pulsed signals is achieved through the modulation of infrared light, while an InGaAs photodiode was used as the receiver for audio signal recovery. As shown in Supplementary Fig.  15, there is no obvious distortion in the received signals, indicating that our system provides sufficient transmission capacity. Owing to the bright radiance and the fast switching ability, the application of our SWIR OLEDs makes light-fidelity (or Li-Fi) communication possible and more flexible. We further demonstrate the real-time transmission of audio signals and pulsed signals through biological tissue (for example, meat or fish slices) ( Supplementary  Videos 1 and 2). We further demonstrate that SWIR OLEDs held great promise for the inspection of semiconductor wafer and chip quality. Since the absorption edge is ~1,100 nm for multi-crystalline silicon and ~1,050 nm for single-crystalline silicon, our IDSe-4Cl device is more advantageous in that its emission is peak located at 1,110 nm compared with a visible-light source. Indeed, as shown in Fig. 5a,b, the SWIR light source shows considerable optical transmission, whereas the wafer is opaque to the visible-light source.
The emission from the IDSe-4Cl OLEDs can penetrate the wafer when illuminated from below and reveal more details, making these OLEDs ideal for industrial applications, such as in the detection of pinholes and cracks in wafers. Snapshot images of the microchip yielded by SWIR irradiance from our devices are shown in Fig. 5c, with the images obtained from visible-light illumination included in Fig. 5d for comparison. The features of the microcircuit and details of defects or cracks can be clearly observed in the SWIR image, whereas part of visible-light image is obscure. In addition, the Y11 device exhibits good operation stability, and shows a half-life operation lifetime (T 50 , the time taken for the radiance to decay to half its initial value) of at least 1,000 h ( Supplementary Fig. 16) at a high current density of 100 mA cm −2 when evaluated under continuous operating conditions and in a glovebox with encapsulation. Other devices based on the IDSe-4F, IDSe-4Cl and COTIC-4F emitters also show comparable lifetime values of 1,000 h ( Supplementary  Fig. 16a). It is worthy of note that the COTIC-4F device shows a longer T 50 of over 500 h when tested in air compared with 300-400 h for other emitters. These findings on large-area devices with high brightness and good stability open up a pathway toward low-cost, portable SWIR OLED light sources for emerging applications.

Conclusion
In summary, we demonstrate OLEDs with bright SWIR emission using finely tuned A-D-A-type molecules as emitters. The resultant OLEDs exhibited very favourable device performance values, including a notable radiance and efficiency in the SWIR region, a very low turn-on voltage at subgap voltages and an even higher efficiency at a high current density of the order of around amperes per cm 2 . We found that the impressive performance of these SWIR OLEDs is essentially due to the excellent photophysical properties of the A-D-A-type molecules, in which their coplanarity, π-conjugated backbone rigidity, extremely small reorganization energies and electron-phonon coupling factors, combined with the heavy-atom substitution that retards high-frequency vibration modes, contributed to significantly suppressed non-radiative recombination rates and improved PLQY values. Furthermore, given their large oscillator strength and their ability to operate at high current density, these A-D-A-type molecules hold the potential to fulfil electrically pumped SWIR lasers. Benefiting from the semi-transparency of biological tissue to SWIR radiation, their high radiation power and the absence of toxic heavy metals in their make-up, our devices provide a promising outlook for a wide range of emerging applications ( Supplementary Fig. 17), such as next-generation optoelectronic devices, wearable biosensors, implantable bioelectronics, IoT (Internet of Things) connectivity and biological imaging.

online content
Any methods, additional references, Nature Research reporting summaries, source data, extended data, supplementary information, acknowledgements, peer review information; details of author contributions and competing interests; and statements of data and code availability are available at https://doi.org/10.1038/ s41566-022-01069-w.

Materials.
The A-D-A-type molecules Y11, SiOTIC-4F and COTIC-4F were obtained as commercial chemicals from 1-Material, and Y6 and BTA3 were purchased from Solarmer. The three twisted small molecules i-IDSe, i-IDSe-4F, and i-IDSe-4Cl were prepared using a synthetic route employed in ref. 51 . Perylene diimide functionalized with amino N-oxide (PDINO) was purchased from Sigma-Aldrich. PEDOT:PSS in aqueous solution was purchased from H.C. Starck. All purchased chemicals were used as received without additional purification.
Unless otherwise stated, all other A-D-A-type molecules were synthesized in the laboratory using a route described in the Supplementary Methods.

Computational methods.
To study the electronic-structure properties of the molecules Y11, IDSe-4Cl and COTIC-4F (discussed in the main text), we carried out quantum-chemical calculations on them. In our calculations, all the long alkyl chains attached to their π-conjugated backbones were replaced by methyl groups, which is a standard procedure for studying electronic structures of single molecules. Molecular aggregation definitely impacts the electronic and optical properties in solid-state films 22 . Many studies have demonstrated that long alkyl chains significantly impact the aggregation structures of the molecules 52,53 , similar to what is observed in the present work. The initial geometries of these three molecules were optimized using the range-separated functional ωB97XD (with a default range-separation parameter ω of 0.2 bohr −1 ) and the 6-31G(d,p) basis set. An iteration procedure 28,54 was used to non-empirically tune the ω parameter with the implicit consideration of the dielectric environment via the polarizable continuum model; the dielectric constant ε was chosen to be 4.5, which is a representative value for non-polar organic semiconductor materials. The TD-DFT approach was used to study the excited-state properties. All quantum-chemical calculations were performed using the Gaussian 16 Rev A03 program 55 . The overlaps between the NTO electron and hole wavefunctions describing the S 1 excited states were quantified using the Multiwfn program 56 .
Optical absorption and photoluminescence characterization. The absorption spectra of the solid-state films were measured using an ultraviolet-visible-NIR spectrophotometer (UV3600, Shimadzu Photoluminescence quantum yield measurements. The absolute PLQY values for emitters with an emission between 300 and 950 nm were measured using an integrating-sphere-coupled spectrometer (QE Pro) and further verified using a commercial absolute PLQY measurement system (C11347-11, Hamamatsu Photonics), while PLQY data for an emission above 950 nm were determined using an integrating sphere and a calibrated spectrometer (NIR Quest 512) as the ratio of the number of photons re-emitted to the number of photons absorbed.
Measurement of time-resolved photoluminescence spectra. The time-resolved PL spectra of the emitters were acquired under ambient conditions of 25 °C using a fluorescence lifetime spectrometer via a time-correlated single-photon-counting technique (Hydraharp 400, PicoQuant). The samples were excited using a femtosecond Ti:sapphire pulsed laser (Coherent) with a pulse duration of 120 fs, a fluence of ~0.2 μJ cm −2 per pulse and a repetition rate of 80 MHz. The PL data were collected using a single-photon-counting photomultiplier tube detector. A longpass filter with a cutoff wavelength at 715 nm or 780 nm was placed before the detector to minimize the scattering of incident laser light.
Device fabrication and characterization. Device fabrication. The devices were fabricated on patterned ITO-coated glass substrates with a sheet resistance of 15-20 ohm per square. The ITO substrates had previously undergone wet-cleaning process in an ultrasonic bath, beginning with acetone, followed by deionized water and isopropanol, before finally being dried in an oven overnight. After air-plasma treatment, a 40-nm-thick PEDOT:PSS (PEDOT:PSS 4083) anode buffer layer was spin-cast onto the precleaned ITO substrate then dried by baking at 150 °C for 20 min. Subsequently, the luminescent small-molecule films (COTIC-4F, IDSe-4Cl, Y11 and so on) were prepared by spin-coating their chloroform solution (with a concentration of 20 mg ml −1 ) at 2,000 revolutions per minute for 30 s to form a uniform 100-nm-thick film on the top of the anode buffer layer. Then a 10-nm-thick PDINO layer was deposited onto the emitting layer by spin-coating from methanol solution (with a concentration of 1.5 mg ml −1 ).
Finally, a 100-nm-thick silver electrode was evaporated with a shadow mask (~2 × 8 mm) in a vacuum chamber at a pressure of 1 × 10 −4 Pa. All device-fabrication processes, except for spin-coating of the PEDOT:PSS layer, were carried out in a nitrogen-filled glovebox (O 2 < 1 ppm, H 2 O < 1 ppm) without exposure to air. We fabricated devices for each emitter at least four times under similar conditions and evaluated at least 15 devices for each emitter reported. Before measurements, the fabricated devices were encapsulated using a glass cover plate and a UV-cured epoxy resin.
Current density-radiance-voltage characteristics and external quantum efficiency measurements. The current density-voltage characteristics of the devices were measured using a Keithley 238 source-meter unit while the radiance-voltage characteristics were simultaneously recorded using a silicon photodiode. The radiance of the SWIR OLEDs was measured by collecting all forward-viewing photons from the device without taking the waveguide modes into account through a lens connected to an integrating sphere. The radiance was calibrated using spectrometers (QE Pro and NIR Quest 512). The InGaAs detector of the spectrometer was calibrated from 900 nm to 1,700 nm using a standard halogen calibration light source (HL-3-plus-INT-CAL), whose wavelength of irradiance ranges from 350 nm to 2,400 nm. The EQE was calculated by dividing the number of photons extracted by the number of electrons injected, per unit time. In the EQE measurements, the number of emitted photons was calculated from the radiance and emission wavelength.
Electroluminescence spectroscopy measurements. The EL spectra for devices with emission peaks between 700 nm and 1,000 nm were recorded using a spectrometer (QE Pro) with a calibrated silicon photodetector. EL spectra for devices with emission peaks past 1,000 nm were recorded using a spectrometer (NIR Quest 512) equipped with an InGaAs line photodetector (calibrated from 900 nm to 1,700 nm).
Operational lifetime measurements. Before operational lifetime measurements, devices were stored in a nitrogen-filled glovebox in the dark. The operational lifetime of the devices was recorded using a commercial system (Life Tester-College Edition, Guangzhou Crysco Equipment) that was equipped with a programmable direct-current power supply (HMC8200) and multiple silicon photodetectors (PDB-C613-2, Lunainc Photonics), where the initial radiant exitance was calibrated using a spectrometer (NIR Quest 512).

Optical wireless communication system setup.
A transistor (model S9013) was used to obtain audio signal amplification and drive the SWIR OLEDs with an active area of 0.16 cm 2 for analogue audio signal transmission. At the receiver end, a high-sensitivity InGaAs photodetector (MTPD1346D-300) was used to convert radiation into photocurrent, which was transmitted to a speaker through a low-voltage audio power amplifier (LM386). For transmission of the pulsed signal, the signal was produced using a function generator (AFG3102C, Tektronix), and the transmitted and received signals were displayed using an oscilloscope (MDO3024, Tektronix) via two independent channels.
SWIR photographs and videos. Photographs and videos of the SWIR light source were obtained using a SWIR camera (LD-SW6401725-CTE2-G (Leading Optoelectronic) or ARTCAM-032 (Artray)) whose detection range was between 950 nm and 1,700 nm with a pixel resolution of 25 μm. Microscopic photographs were taken using a transflective polarizing microscope (XP4A, SHMLT) equipped with a visible-light CCD, and the SWIR photographs were recorded by switching the self-equipped CCD to the SWIR camera.

Data availability
The data that support the findings of this study are available from the corresponding author upon reasonable request. Source data are provided with this paper.