This preprint is under consideration at Applied Biochemistry and Biotechnology. A preprint is a preliminary version of a manuscript that has not completed peer review at a journal. Research Square does not conduct peer review prior to posting preprints. The posting of a preprint on this server should not be interpreted as an endorsement of its validity or suitability for dissemination as established information or for guiding clinical practice.
Learn more about In Review
Research Article
Y.J. Zhou
North China University of Science and Technology
Corresponding Author
ORCiD: https://orcid.org/0000-0001-6498-385X
License:
This work is licensed under a CC BY 4.0 License. Read Full License
This study solidifies the aeolian sand by microbial induced carbonate precipitation (MICP) technique. The effects of cementation solution with different concentrations, particle size, and grouting batches are examined via the bender element, unconfined compressive test and scanning electron microscope (SEM). The bender element results show that the wave speed of loose aeolian sand is 200m/s; however, after solidify the aeolian sand, the speed of P-wave is about 450-600m/s and S-wave is about 350-500m/s. Additionally, the unconfined compressive strength (UCS) results indicate that when the concentration of cementation solution is 0.75mol/L, the UCS of bio-solidified sand sample is the highest. Then, compared with the aeolian sand with original grade, the particles ranging from 0.1-0.4mm have a better cementation effect. Moreover, the UCS of bio-solidified sand samples increases along with the grouting batch. From the SEM images, it can be seen that when the grouting batch reaches to five times, the particles are almost completely covered by CaCO 3 crystals compared with the three batches and four batches.
Keywords
MICP, aeolian sand, solidification, bender element, UCS, SEM
Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12
Figure 13
Figure 14
Figure 15
Figure 16
Figure 17
Loading...
Badges
Prescreen
This manuscript passed our Prescreen assessment
Complete author information
Appropriate declaration statements
Potential risks to human health
Prescreen
Peer Review Timeline
CURRENT STATUS: Under Review
Version 1
Posted 22 Mar, 2021
No community comments so far
Review #? received
Received 01 Mar, 2021
Reviewers invited
Invitations sent on 01 Mar, 2021
Editor invited
On 21 Feb, 2021
First submitted
On 18 Feb, 2021
Metrics
Comments: 0
PDF Downloads: ...
HTML Views: ...
Learn more about our company.
This preprint is under consideration at Applied Biochemistry and Biotechnology. A preprint is a preliminary version of a manuscript that has not completed peer review at a journal. Research Square does not conduct peer review prior to posting preprints. The posting of a preprint on this server should not be interpreted as an endorsement of its validity or suitability for dissemination as established information or for guiding clinical practice.
Learn more about In Review
Research Article
Y.J. Zhou
North China University of Science and Technology
Corresponding Author
ORCiD: https://orcid.org/0000-0001-6498-385X
Badges
Prescreen
This manuscript passed our Prescreen assessment
Complete author information
Appropriate declaration statements
Potential risks to human health
Prescreen
Peer Review Timeline
CURRENT STATUS: Under Review
Version 1
Posted 22 Mar, 2021
No community comments so far
Review #? received
Received 01 Mar, 2021
Reviewers invited
Invitations sent on 01 Mar, 2021
Editor invited
On 21 Feb, 2021
First submitted
On 18 Feb, 2021
License:
This work is licensed under a CC BY 4.0 License. Read Full License
This study solidifies the aeolian sand by microbial induced carbonate precipitation (MICP) technique. The effects of cementation solution with different concentrations, particle size, and grouting batches are examined via the bender element, unconfined compressive test and scanning electron microscope (SEM). The bender element results show that the wave speed of loose aeolian sand is 200m/s; however, after solidify the aeolian sand, the speed of P-wave is about 450-600m/s and S-wave is about 350-500m/s. Additionally, the unconfined compressive strength (UCS) results indicate that when the concentration of cementation solution is 0.75mol/L, the UCS of bio-solidified sand sample is the highest. Then, compared with the aeolian sand with original grade, the particles ranging from 0.1-0.4mm have a better cementation effect. Moreover, the UCS of bio-solidified sand samples increases along with the grouting batch. From the SEM images, it can be seen that when the grouting batch reaches to five times, the particles are almost completely covered by CaCO 3 crystals compared with the three batches and four batches.
Figure 1
Figure 2
Figure 3
Figure 4
Figure 5
Figure 6
Figure 7
Figure 8
Figure 9
Figure 10
Figure 11
Figure 12
Figure 13
Figure 14
Figure 15
Figure 16
Figure 17
Loading...