Background: The aim of current study was to evaluate and compare the influence of Dycal, Lime-lite, Theracal LC, Biodentine, Resin-modified glass ionomer cement (RMGIC), and Activa Bioactive as the pulp capping material on the shear bond strength of resin composite to dentin.
Methods: A total of 70 extracted caries-free molars were randomly assigned to seven groups. Six test groups were covered with various protective liners: Dycal (GD), Theracal LC (GT), lime-lite (GL), Activa Bioactive (GA), Biodentine (GB), RMGIC (GR). The control group (GC)received no liner pretreatment. Each sample was bonded to resin composite using the total-etch tetric N bond adhesive. The samples were then tested for shear bond strength using the universal testing machine at a cross-head speed of 1 mm/min until bond failure occurred. The data were analyzed using the one-way ANOVA test followed by the Tamhane post-hoc test for pairwise comparisons of the groups
Results: Independent of the type of the applied liner, all groups exhibited inferior SBS to dentine compared to the control group. GT and GR showed significantly higher shear bond strength than GB and GD, which showed the lowest shear bond strength. GL and GA also had significantly lower SBS results than GT. The mode of fracture was predominantly cohesive in GD, GB, and GT and adhesive in GA.
Conclusion: This present study concludes that the bond strength of resin-composite to dentine can be affected differently using various types of liners.