Abstract
In this work, a laser polishing-hardening (LPH) method with integration and high efficiency for the treatment of AISI D2 tool steel was proposed, and the effects of laser hardening (LH), laser polishing (LP) and LPH treatments on the surface topography and microhardness were examined. The results show that LH method had a negligible effect on the surface roughness of the treated sample, while the surface roughness Ra of LP and LPH specimens was reduced by 74.6% and 80.9% respectively, indicating that the milled surface topography had been significantly improved, especially LPH was more effective in reducing the roughness. Besides, the polishing efficiency of LPH was 10 times that of LP approach. In terms of hardness improvement, the near-surface microhardness of LH and LPH samples increased by 1.5 times and 1.3 times respectively, and the effective hardened zone (EHZ) depth was 0.42 mm and 0.24 mm respectively, demonstrating that these two laser processing methods had a beneficial effect on the cross-section microhardness of D2 tool steel, while the increase of LP on the microhardness was insignificant. The comprehensive analysis of the surface morphology and microhardness of LPH specimen indicates that LPH was a feasible laser surface treatment method for D2 tool steel. On the premise of ensuring a high surface finish, the polishing efficiency can be remarkably improved, the subsurface microhardness and EHZ depth of processed specimen can be also significantly enhanced, which provided a feasible idea for the application of laser surface treatment technology in industrial mold production.