Frank-Kasper phase is a class of ordered crystals composed of the topologically close-packed atomic-layers [1, 2], in which the atoms with a smaller radius form as the close-packed planes and the atoms with a larger radius embed in the tetrahedral gaps. So far, there have 28 different types of Frank-Kasper phases found experimentally (in Supplemental Table S1), including in metal alloys [3, 4], inorganic colloids [5, 6], and soft matters [7-10].
Generally, the Frank-Kasper phases can be considered as ordered approximates of quasi-periodic crystals due to some shared construction rules from atomic clustering and stacking [11]. Since the Al-Mn icosahedral quasicrystal discovered in 1984 by Shechtman et al [12], the complex architectures of Frank-Kasper phases are considered as a link between the traditional simple periodic structures (such as the face-centered cubic, hexagonal close-packed, and body-centered cubic structures) and quasicrystals [10, 13].
From the viewpoint of crystallography characteristics, there are two types of Frank-Kasper structures which be constructed by three basic units of A15 (representative alloy: Cr3Si), C15 (representative alloy: MgCu2), and Z (representative alloy: Zr4Al3) fundamental structures frequently observed to date, i.e., the pentagonal Frank-Kasper phases and the hexagonal Frank-Kasper phases [14, 15]. The pentagonal Frank-Kasper structure (see Supplemental Figure S1) can be considered as a periodic arrangement of icosahedron (coordination number (CN) = 12) columns along the pseudo 10-fold axis promoting the formation of C15 (parallelogram) and Z (rectangle) plane tiling patterns, and the parallelogram and rectangular patterns self-assemble under some geometrical constraints to generate the present pentagonal phases. Similarly, the hexagonal Frank-Kasper phases (see Supplemental Figure S2) can be regarded as a structure formed by the icositetrahedron (CN = 14) columns arranged periodically along the pseudo 12-fold axis, to build square A15 and rhombic Z plane tiling patterns, and the bonding of the two patterns leads to the generation of the hexagonal phases.
To better understand the relationship between these Frank-Kasper structures, Fig. 1 provides a relationship between the average CN and the fraction of CN = 15 polyhedra in a Frank-Kasper phase, and all these 28 types of Frank-Kasper phases are located in a triangle with the three basic Frank-Kasper structures located at three vertices. In which the pentagonal Frank-Kasper phases assembled by the C15 and Z plane tiling patterns are represented by the red balls; the hexagonal Frank-Kasper phases assembled by the A15 and Z plane tiling patterns are represented by the blue balls. The Z phase structure, the basic unit of both the pentagonal phases and the hexagonal phases, is represented by a ball with red and blue colors. We defined here the three fundamental structures of A15, C15, and Z phases as the first-order Frank-Kasper phases, and the complex phases assembled by any of three basic units as the second-order Frank-Kasper phases. And it can be found that the Z phase is the most important since it is the basic unit for assembling any of the second-order Frank-Kasper phases.
At present, the C15 fundamental Laves structure with a chemical formula of AB2 and the A15 fundamental structure with a chemical formula of A3B are found abundantly in metal alloys, and there are more than 900 kinds of Laves phases have been identified experimentally [3], and the high-temperature superconductors with A15 structure (such as Nb3B, Nb3Si, and Nb3Ge) also exist extensively. However, the Z phase structure with a A4B3 chemical formula postulated by Frank & Kasper in 1959 are rarely observed to date [2]. Since a Zr4Al3 phase was proposed firstly by C. G. Wilson et al. in 1960 [16], this structure has not been confirmed by any other direct experimental observations to date except a recent report in soft matter [10]. And these two Z phases in both alloy and soft matter are three-dimensional blocks to maintain their thermodynamical stability.
In contrast, we reported here a new structured 2D Frank-Kasper Z phase in an aged Mg-Sm-Zn model system. More interestingly, the 2D Frank-Kasper Z precipitate with only one unit-cell height in the Z axis, and it is thermodynamically metastable. This finding would pave a way for understanding the formation mechanism of the second-order Frank-Kasper phases and quasicrystals in general condensed matters.
A Mg-4Sm-2Sm (in wt.%) alloy was induction-melted and solution-treated at 520 °C for 12 h, followed by aging at 200 °C for 48 h (the experimental details are in the Supplemental Materials). The HAADF-STEM images of the aged-sample, viewed along the α, α, and α directions, are shown in Fig. 2. Low-magnification HAADF-STEM images (Figs. 2a-c) show that there are high-density nanosized precipitate-plates distributed in the α-Mg grains, whose length is approximately 30~50 nm, with a height less than 1 nm lying on the {0001}α basal planes. Bright-filed images and corresponding select-area electron diffraction (SAED) patterns are provided in Supplemental Figure S3. This precipitate has been named by γ” phase in the field of magnesium alloys, but its fine structure has not been well documented [17-19].
To precisely reveal the crystal structure and atomic coordinates of the precipitate-plates, atomic imaging by HAADF-STEM was used. Atomic-scale HAADF-STEM image of the precipitate-nanoplates in Fig. 2a, is enlarged and shown in Fig. 2d. The α enlarged image shows that there are many bright dots inside the precipitate-nanoplate, and each bright dot represents a Sm-rich atomic column because the brightness of individual atomic column in HAADF-STEM image approximates the square of the average atomic numbers (the atom number is 12 for Mg, 30 for Zn, and 62 for Sm) [20, 21]. The Sm-enriched atomic columns distribute along the < >α directions and are separated by a constatnt distance. It can thus be concluded that the precipitate-nanoplate with an ordered hexagonal structure, and the corresponding lattice image is highlighted by a red 60° rhombus in the top-right inset in Fig. 2d. The crystal lattice constant of a can also be measured to be ~5.56 Å.
Local part of the precipitate-nanoplates in Fig. 2b is further enlarged and shown in Fig. 2e. The α enlarged image shows that the brightest dots located in the sub-outer layer correspond to the Sm atomic columns and the bright dots distributing on the central layer correspond to the Zn atomic columns with the help of the Z-contrast of Sm and Zn, which are represented by the blue and yellow circles in Fig. 2e, respectively. As a result, the precipitate-nanoplate is consisted of five atomic layers, i.e., the Mg / Sm / Zn / Sm / Mg atomic stacking structure, as displayed in the inset of Fig. 2e. And the atomic inter-distances of hSm-Sm and hMg-Mg can be measured to be ~ 3.49 Å and ~ 4.83 Å, respectively.
More evidences can be found from the HAADF-STEM image, detected along the α direction (Fig. 2f). The Zn atomic columns, as marked as the yellow solid-circles, always locate in the middle of four neighboring Sm atomic columns, and the Zn-dots wih weaker contrast can also be detected and hide between the two brighter contrast Sm atomic columns, as indicated in the yellow dashed-circles in inset of Fig. 2f. The results above indicate that the central-layer Zn atoms has a new grid structure that incoherent with (0001)α atomic layer.
Based on the atomic-scale HAADF-STEM results mentioned above, a new structured 2D Frank-Kasper Z phase model for the precipitate-nanoplate can be constructed. Modeled atomic arrangements and clusters of the 2D Frank-Kasper Z phase are displayed in Fig. 3, in which the Mg, Sm and Zn atoms are presented by the red, blue, and yellow spheres, respectively. And the structural information of the Frank-Kasper Z phase, as well as the atomic coordinates are presented in Supplemental Table S2. The most unique features of the Frank-Kasper Z phase, i.e., the rhombic tiling units (blue rhombic) formed by a periodic arrangement of the icositetrahedron clusters (cyan circle) in the Z axis, and the rectangle tiling units (red rectangle) generated by a periodic arrangement of the icosahedron columns (yellow circle) along the Z direction, can be observed clearly in Figs. 3a and 3b. The two outmost layers correspond to the Mg atoms, and the distance between adjacent Mg atoms is ~ 3.21 Å. Moreover, one Mg atom is surrounded by three equilateral hexagons, which means that the grid type of the close-packed plane is 63. In the sub-outer layer, inter-distance of the Sm atoms is ~ 5.56 Å, and a 36 grid structure can be detected. In the central layer, as occupied by the Zn atoms, a 3636 grid can be found, which corresponds to the “equilateral triangle - equilateral hexagon - equilateral triangle - equilateral hexagon” structure. Inter-distance between the Zn atoms is ~ 2.78 Å. And the five-layer unit-cell, with three types of grid structures, forms a “63+36+3636+36+63” topologically close-packed structure with thickness of ~ 4.83 Å in the α direction. Finally, the chemical formula of the 2D Frank-Kasper Z precipitate can be determined to be Mg2Sm2Zn3.
Simulated electron diffraction patterns of the new generated Z-Mg2Sm2Zn3 model and the corresponding SAED patterns of the precipitate-plate in the α-Mg matrix are presented in the Supplemental Fig. S4. It can be found that the simulation results are well consistent with the experimental observations, further verified the validity of the structure we constructed.
Generally, the atomic clusters have a higher stacking density and a lower free energy of system [1, 2, 22]. Fig. 3d exhibits a 3D icosahedron cluster model in the Z-Mg2Sm2Zn3 precipitate along the Z direction, and an atomic number of “…1-5-1-5-1…” chain structure can be observed, suggesting that the central atom (Zn atom-sphere) is in contact with 12 atom-spheres. Fig. 3e presents a 3D view of icositetrahedron chain structure model with an atomic number of “…1-6-1-6-1…”, and the Sm atom-sphere is located at the central position. In this configuration, the top sphere (dotting blue sphere) is the adjacent to Mg atom in the matrix only then can form such a polyhedron with a CN of 14, since the 2D structure is confined in the Z direction. Unfortunately, what it needs to be pointed out is that the icositetrahedron with CN = 14 has not been observed yet in this system. However, Fig. 3f provides a novel 3D irregular polyhedron with a CN of 16 which is confirmed by experimental observations, and the top spheres (3 solid red spheres) are also adjacent to the matrix Mg atoms, and thus can generate such a chain structure with an atomic number of “3-6-1-6-1”.
The results of first-principles calculations for the 2D Frank-Kasper Z-Mg2Sm2Zn3 phase are provided in Fig. 4 and the Supplemental Table S3. An unrelaxed structure with a stacking sequence of “ACA”, i.e., the initial state of the precipitate-plate without considering lattice distortion and rearrangements of atoms, is shown in Fig. 4a. In which the atomic layer “A” is completely consistent with the matrix layer, and just some Mg positions are replaced orderly by the Sm atoms. The corresponding geometry relaxed structure is presented in Fig. 4b. Obviously, the optimized structure is different from the initial state, a simple atomic shuffling by self-adaption, can transform the monoatomic “A” layer to a double-layers structure (marked as “A’”) containing Mg and Sm atomic layer, achieving the transition from simpler crystal to the complex close-packed structure. In addition, the formation energy of the 2D Z-Mg2Sm2Zn3 precipitate is 38.54 meV, meaning that such a structure cannot generated independently. Fig. 4c shows an optimized “ABA-A’CA’-AB” sandwiched model containing matrix Mg layers. The bonding of “A-A’” layers means that the ideal icositetrahedrons with CN = 14 mentioned above in Fig. 3e are generated, however, this state is thermodynamically metastable, with a formation energy of only -18.79 meV. The experimentally observed sandwiched model with a stacking sequence of “BAB-A’CA’-BA” (in Fig. 2f) is also optimized, and presented in Fig. 4d. The connection of “B-A’” layers then form the irregular polyhedron with a CN of 16 mentioned above in Fig. 3f. The formation energies of such a structure is -88.19 meV, indicating that this configuration is thermodynamically more stable. And lattice parameters (Fig. 4d) of the optimized structure are well consistent with the experimental measurements. Moreover, it is worth mentioning that traditional Frank-Kasper twenty-eighth polyhedron with CN = 16 is totally different from the irregular polyhedron determined here [23].
The charge distribution of the “BAB-A’CA’-BA” sandwiched model viewed along the Z direction is shown Fig. 4e. It can be found that there is a mass of electrons accumulated at the Z-Mg2Sm2Zn3/α-Mg hetero-interface, and less charge distributed in the central Zn layer, indicating that the Mg and Sm atoms on the outermost layers bonding stronger. Additionally, the electron localized function results exhibited in Figs. 4f-i illustrates same conclusion as the charge distribution analysis, that is, obviously covalent characteristic bonding in the outermost layers, and weaker bonding in the central Zn layer.
The formation of Frank-Kasper Z phases is usually inhibited due to a relatively large volume ratio among the its constituents [9, 10, 24]. Since the first proposed of the Zr4Al3 phase by C. G. Wilson et al in 1960 based on X-ray diffraction results [16], the structure has not been confirmed by any other TEM experimental observations to date. However, we unambiguously confirmed here the existence of a 2D Frank-Kasper Z fundamental structure with only one unit-cell thickness in the crystallography. It should be noted that the validated 2D Frank-Kasper Z structure is a meta-stable phase, as evidenced by TEM analysis in Supplemental Fig. S5, and the Z-Mg2Sm2Zn3 precipitate would generate more stacking faults with a prolonged ageing.
In conclusion, we have identified a new type of 2D Frank-Kasper Z phase precipitated in a model Mg-Sm-Zn ternary system. Based on the atomic-scale HAADF-STEM observations combined with DFT computations, the crystal structure, chemical composition, and the atomic coordinates of the Z precipitate-plate are fully unraveled. The confined Z-Mg2Sm2Zn3 phase has an ordered hexagonal structure (space group: P6/mmm, a = 5.56 Å, c = 4.83 Å), and with one unit-cell height in the α direction. The 2D Z-Mg2Sm2Zn3 phase has a stacking sequence of “…-AB-A’CA’-BA-…” along the α axis. A new structured Frank-Kasper cluster model with CN = 16 has been confirmed. This finding is interesting and important to understand the formation mechanism and clustering behavior of the Frank-Kasper phases, and a new class of 2D Frank-Kasper Z phases with A2B2C3 in composition would be established in follow-up studies in the near future. It is also expected to provide a meaningful theoretical guidance for designing and developing novel high-strength alloys strengthened by the 2D Frank-Kasper Z precipitates.